Search results

Understanding employees’ multi-dimensional motivations is at the core of realizing the potential of a well-designed human resource (HR) system. This study aims to investigate whether the effects of HR practices on employee motivations, and their performance would be dependent on the service orientation of HR department.

The authors collected data in two surveys: a pilot survey and a main survey with a two-wave design. The pilot survey with 93 respondents was to verify the newly developed HR service orientation scale. In the main survey, a total of 276 supervisor-subordinate pairs from 48 companies were valid for analysis.

The authors find support for their hypothesis that promotion-oriented motivation mediates the relationship between discretionary HR practices and employee outcomes [in-role performance and organizational citizenship behavior (OCB)]. Furthermore, the indirect effect of discretionary HR practices on employee outcomes is stronger when the HR service orientation is higher. Transactional HR practices, however, are not evidenced to relate to employee prevention-focused motivation and outcomes.

The findings illustrate a comprehensive process of HR practices on employees’ multi-dimensional motivations. High service skills of HR professionals in handling internal employees’ needs could amplify employees’ promotion-focused motives, which in turn increase their in-role performance and OCB.

In sum, the authors' study contributes to both human resource management (HRM) and employee motivation literature by demonstrating the different impacts of discretionary and transactional HR practices on employees’ motivations. In addition, by revealing HR service orientation as an important contingency factor, the authors shed greater light on when and how HR practices can motivate employees.

This paper aims to explore the influence of corrosion-deformation interactions (CDI) on the corrosion behavior and mechanisms of 316LN under applied tensile stresses.

Corrosion of metals would be aggravated by CDI under applied stress. Notably, the presence of nitrogen in 316LN austenitic stainless steel (SS) would enhance the corrosion resistance compared to the nitrogen-absent 316L SS. To clarify the CDI behaviors, electrochemical corrosion experiments were performed on 316LN specimens under different applied stress levels. Complementary analyses, including three-dimensional morphological examinations by KH-7700 digital microscope and scanning electron microscopy coupled with energy dispersive spectroscopy, were conducted to investigate the macroscopic and microscopic corrosion morphology and to characterize the composition of corrosion products within pits. Furthermore, ion chromatography was used to analyze the solution composition variations after immersion corrosion tests of 316LN in a 6 wt.% FeCl₃ solution compared to original FeCl₃ solution. Electrochemical experiment results revealed the linear decrease in free corrosion potential with increasing applied stress. Electrochemical impedance spectroscopy results indicated that high tensile stress level damaged the integrity of passivation film, as evidenced by the remarkable reduction in electrochemical impedance. Ion chromatography analyses proved the concentrations increase of NO₃⁻ and NH₄⁺ ion concentrations in the corrosion media after corrosion tests.

The enhanced corrosion resistance of 316LN SS is attributable to the presence of nitrogen.

The scope of this study is confined to the influence of tensile stress on the electrochemical corrosion of 316LN at ambient temperatures; it does not encompass the potential effects of elevated temperatures or compressive stress.

The resistance to stress electrochemical corrosion in SS may be enhanced through nitrogen alloying.

This paper presents a systematic investigation into the stress electrochemical corrosion of 316LN, marking the inaugural study of its impact on corrosion behaviors and underlying mechanisms.